High density and high strength sintered machine parts
High strength by high density and high precision are achieved.
Material
| Material Code | Chemical Components(wt.%) | ||||
|---|---|---|---|---|---|
| Fe | Ni | Mo | C | Other | |
| Z34 | Residual Amount | 1∼3 | 0.5∼1.5 | 0.1∼0.3 | 1max. |
Mechanical characteristic
| Material Code | Heat Treatment | Density (g/cm³) |
Tensile Strength (MPa) |
Young's Modulus (GPa) |
Poisson's Ratio (MPa) |
Elongation (%) |
Apparent Hardness (HRA) |
|---|---|---|---|---|---|---|---|
| Z34 | Quench-and-Temper | 7.3 | 945 | 172 | 0.28 | 0.73 | 77 |
Note：The above numerical value is the measure, and not the certified value.